Obtenção e caracterização de artefatos de cimento com adição de cinzas pesadas de carvão mineral

Autores

  • Cláudia Terezinha Kniess¹ ¹Universidade Ibirapuera Av. Interlagos 1329 - São Paulo - SP
  • Carlindo Baeta de Oliveira¹ ¹Universidade Ibirapuera Av. Interlagos 1329 - São Paulo - SP
  • Luciano Borgonovo ² ²Serviço Nacional de Aprendizagem Industrial - SENAI - SC
  • Bruno Moreira de Aguiar³ ³Instituto de Pesquisas Energéticas e Nucleares - IPEN - SP
  • Patrícia Bodanese Prates Universidade Federal de Santa Catarina - UFSC

Palavras-chave:

Cinza Pesada de Carvão Mineral, Blocos de Concreto, Propriedades Mecânicas

Resumo

As características físicas, químicas e mineralógicas das cinzas pesadas de carvão mineral, geradas nas usinas termelé- tricas, são compatíveis com várias matérias-primas utilizadas nas indústrias cerâmicas, o que indica uma possibilidade de substituição parcial ou integral destas matérias-primas por este resíduo, formado majoritariamente por quartzo (SiO2 ) e mulita (3SiO2 .2Al2 O3 ). A possibilidade da utilização das cinzas pesadas de carvão mineral na produção de artefatos de cimento é uma alternativa para minimizar problema de meio-ambiente. Para isso, é necessário que o material apresente características competitivas e processo de produção economicamente viável. Este trabalho tem como objetivo avaliar a possibilidade da utilização das cinzas de carvão mineral, estabilizadas com cal hidratada, como matéria-prima de baixo custo e alto valor agregado, reduzindo assim o impacto ambiental causado pela disposição do mesmo. Foram desenvolvidas duas formulações utilizando cinzas pesadas de carvão mineral e cal hidratada em diferentes percentuais. Os parâmetros experimentais variáveis foram o percentual de água utilizado na moldagem dos blocos, a pressão de conformação e o tempo de cura, buscando otimizar a condição que apresenta as melhores propriedades mecânicas.

Palavras-chaves: Cinza Pesada de Carvão Mineral, Blocos de Concreto, Propriedades Mecânicas.

Abstract


The physical characteristics, chemistries and mineralogical of the mineral coal bottom ashes, generated in the thermal electric plant, are compatible with several raw materials used in the ceramic industries, what indicates a possibility of substitution partial or integral of these raw materials for this residue, formed for the most part by quartz (SiO2 ) and mullite (3SiO2 .2Al2 O3 ). The possibility of the use of mineral coal bottom ashes in the production of concrete workmanships is an attractive alternative to minimize environment problems. For such, it is obviously necessary that the use of that residue as raw material leads to the production of a material with characteristics appropriate and economically competitive. This work has as objective verifies the possibility of use of the mineral coal bottom ashes, stabilized with moisturized whitewash, as raw material in the production of concrete blocks, seeking to reduce the environmental impact caused by the by-product and to join commercial value to the same. Two formulations were developed using coal bottom ashes and moisturized whitewash with percentiles different. The variable experimental parameters were the percentile of water used for the molding of the blocks, the conformation pressure and the cure period, looking for to optimize the condition with the best mechanical properties.

Keywords: Mineral Coal Bottom Ash, Concrete Blocks, Mechanical Properties.

 

Referências

Chies, F, Zwonok, O, SILVA, N, W. Desenvolvimento de blocos e tijolos a partir de cinzas de fundo. Coletânea Habitare: Utilização de resíduos na construção habitacional.v.4; 1995.

Pozzobon, C. E. Aplicações tecnológicas para a cinza do carvão mineral produzida no Complexo Termelétrico Jorge Lacerda. Dissertação de Mestrado em Engenharia Civil. Universidade Federal de Santa Catarina. Florianópolis; 1999.

ABNT - Associação Brasileira de Normas Técnicas - NBR 7173/82 - Blocos vazados de concreto de concreto simples para alvenaria sem função estrutural. Rio de Janeiro; 1980.

ABNT - Associação Brasileira De Normas Técnicas - NBR 6136/80 - Blocos vazados de concreto simples para alvenaria estrutural. Rio de Janeiro; 1980

JCPDS - Joint Committee of Powder Diffraction Standards. International Centre for Diffraction Data. Pennsylvania, USA; 1981.

ICSD - Inorganic Crystal Structure Database. GmchinIntitut fur Anorganishe Chemie and Fachinformationzentrum FIZ. Karlsruhe, Germany; 1995.

Downloads

Publicado

2011-12-21

Edição

Seção

Artigos